L.Chen
,
Y.F. Han
,
C.H Tao and M.L. Xie(Beijing Institute of Aeronautical Materials
,
Beijing 100095
,
China Manuscript received 26 August 1996)
金属学报(英文版)
The microstructures of NiAl(Co)-TiB_2 composite prepared using exothermal dispersion (XD) method have been studied by optical microscopy, XRD, EDS, and TEM The results show that, TiB_2 paritcles are typically single crystal, and fairly uniformly distributed. The matrix mainly consists of β-NiAl phase, Ll_2γ′Ni_3Al phase and δ-Ni_3Al phase. The δNi_3Al has a fcc crystal structure with lattice parameter a=1.068nm.The data of compressive testing at room temperature show that the room temperature ductility of NiAl(Co) matrix composite is much better than that of stoichiometric NiAl.
关键词:
:intermetallic compound
,
null
李谷松
,
丁炳哲
,
苗卫方
,
叶荔蕾
,
郭建亭
金属学报
用球磨机分别对Ｎｉ－５０ａｔ．－％Ａｌ和Ｎｉ－２５ａｔ．－％Ａｌ混合粉末进行机械合金化，并对Ｎｉ_３Ａｌ预合金粉末进行高能球磨，观察了粉末的金相组织，测定了粉末的硬度、平均直径和晶粒尺寸，并作了ＸＲＤ物相分析结果表明，经３ｈ研磨，Ｎｉ－５０ａｔ．－％Ａｌ混合粉末变成ＮｉＡｌ金属间化合物，其晶粒直径约５ｎｍ；经５ｈ机械球磨，Ｎｉ－２５ａｔ．－％Ａｌ混合粉末成为无序的亚稳定Ｎｉ固溶体，而Ｎｉ_３Ａｌ预合金粉末由Ｌｌ_２型长程有序金属间化合物转变为ｆｃｃ无序固溶体；球磨更长时间，则形成纳米晶．
关键词:
金属间化合物
,
mechanical alloying
,
nanocrystalline structure
,
Ni
,
Al
,
Ni_3Al
,
NiAl
曾潮流
,
张鉴清
,
吴维玟
,
郭建亭
金属学报
研究了Ｎａ_２ＳＯ_４沉积盐引起的Ｎｉ_３Ａｌ－Ｆｅ于７００一８２０℃空气中的腐蚀行为。结果表明，Ｎｉ_３Ａｌ－Ｆｅ遭受自持性的热腐蚀。热腐蚀的发生似可归因于Ｆｅ与Ｎａ_２ＳＯ_４反应的产物Ｎａ_２Ｏ与Ｎａ_２ＳＯ_４形成了Ｎａ_２Ｏ－Ｎａ_２ＳＯ_４共晶熔融盐，随后合金中Ｍｏ的氧化产物ＭｏＯ_３参与电化学阴极还原反应，从而引发合金快速的热腐蚀。此外，熔盐中Ｎａ_２ＳＯ_４与ＭｏＯ_３反应生成的ＳＯ_３导致了熔盐的高酸度和合金的内硫化，从而进一步加剧了腐蚀的进程。
关键词:
金属间化合物
,
Ni_3Al-Fe
,
Na_2SO_4 hot corrosion
,
null